ALÜMİNA ASTAR
ALÜMİNA ASTAR
Aşınmaya dayanıklı seramik astar, aşınma direnci, korozyon direnci, yüksek sıcaklık direnci, darbe direnci ve kolay yapı özelliklerine sahiptir.
| TEKNİK ÖZELLİKLER |
|---|
| TEST DEĞERLERİ |
| 30# SIC Sand Breeze |
| Breeze Speed 35 m/s |
| Angle of Breeze 450 |
| Breeze Distance 5 cm |
| TEKNİK ÖZELLİKLER |
|---|
| ORTALAMA AŞINMA DEĞERLERİ |
| Loss Weight (g) 4.1 |
| Loss Bulk (cm3) 1.138 |
| Loss Weight (mm) 1.425 |
| Wear Rate In Bulk 219 |
| TEKNİK ÖZELLİKLER |
|---|
| STANDART ÖLÇÜLER |
| 24 x 24 x 10 + 0.2mm |
| 24 x 12 x 10 + 0.2mm |
| 20 x 20 x 5 + 0.2mm |
| 20 x 20 x 4 + 0.2mm |
| 17.5 x 17.5 x 5 + 0.2mm |
| 17.5 x 17.5 x 4 + 0.2mm |
| 17.5 x 17.5 x 3 + 0.2mm |
| 10 x 10 x 4 + 0.1mm |
| 10 x 10 x 3 + 0.1mm |
| TEKNİK ÖZELLİKLER | |||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| TANIM | Al2O3 | SiO2 | Bulk density (g/cm3) | Hardness (Mohs) | Hardness (GPa) | Water Absorptions | Bending Strength (MPa) | Compression Strength (GPa) | Thermal Condustivity | E-Modulus (GPa) | |||||
| %92 YOĞUNLUKLU ALÜMİNA ASTAR TEKNİK DETAYLARI | ≥92% |
≤4% |
≥3.60 |
≥9 |
11.8 Hv1.0 |
0.01 |
≥340 |
≥2.5 |
20C (W/ 16 m.k) |
280 |
|||||